Synthesis and characterization of nano-ceramic pigment Co_0.5Zn_0.5Al₂O₄ via polyacrylamide gel method

Abstract

Purpose

The purpose of this paper is to synthesize and characterize nano-ceramic blue pigment Co_0.5Zn_0.5Al₂O₄ via polyacrylamide gel method. Generally, the high cost and the environmental toxicity of cobalt aluminate pigments lead them to become less common and cause problems in production process. To significantly reduce this problem, it is required to reduce the cobalt in the pigment and replace the cobalt with some amounts of zinc in the structure.

Design/methodology/approach

In this paper, calcination temperature and its effects on phase specification and color properties of final product were investigated. The powders were studied by using XRD, FESEM, TG/DTA, FTIR, UV-Vis and colorimetric in CIELab space, in which the calcination temperatures were set to 600°C, 800°C and 1,000 °C, and the inert atmosphere was air.

Findings

According to the XRD patterns, single-phase spinel structure with a good crystallinity was formed even in the low temperature. The infrared spectra displayed vibrations at about 500, 560 and 680 cm⁻¹, which were ascribed to the spinel structure. FESEM images showed nanoscale particles with an average size of 32 nm. Regarding the Co²⁺ spin transitions in tetrahedral sites, the UV-Vis spectra presented three bands at 552, 598 and 628 nm.

Practical implications

The colorimetric data indicated the formation of blue pigments corresponding to negative values of b*. The color of pigments was affected by calcination temperature.

Originality/value

The characterization analysis shows that a blue pigment has been obtained in this research. Different degrees of blue color were obtained at different calcination temperatures.

Citation

Rahimian, M., Saebnoori, E. and Hassanzadeh-Tabrizi, S.A. (2020), "Synthesis and characterization of nano-ceramic pigment Co_0.5Zn_0.5Al₂O₄ via polyacrylamide gel method", Pigment & Resin Technology, Vol. 49 No. 3, pp. 189-195. https://doi.org/10.1108/PRT-07-2019-0062