SURFACE REACTIONS DURING METAL FATIGUE
Abstract
In metal fatigue tests at the National Bureau of Standards, numerous gas bubbles formed under transparent tape applied to the surfaces of flat specimens. A mass spectrometric analysis indicated that the evolved gas was hydrogen. This work provides evidence of a correlation between surface reactions due to the environment and fatigue damage in metals.
Citation
(1963), "SURFACE REACTIONS DURING METAL FATIGUE", Anti-Corrosion Methods and Materials, Vol. 10 No. 1, pp. 16-18. https://doi.org/10.1108/eb020033
Publisher
:MCB UP Ltd
Copyright © 1963, MCB UP Limited